Topical IL@MOF-based (ad)sorbents for Gas Separation
| datacite.subject.fos | Engenharia e Tecnologia::Engenharia Química | pt_PT |
| dc.contributor.advisor | Esteves, Isabel | |
| dc.contributor.advisor | Esperança, José | |
| dc.contributor.author | Keba, Anastasiia | |
| dc.date.accessioned | 2022-04-07T10:41:34Z | |
| dc.date.available | 2022-04-07T10:41:34Z | |
| dc.date.issued | 2021-02 | |
| dc.description.abstract | De ano para ano as emissões de gases com efeito de estufa aumentam. O CO2 é emitido para a atmosfera a partir da combustão de combustíveis fósseis e, a longo prazo, origina problemas ambi-entais, energéticos e económicos. O seu impacto nas alterações climáticas é elevado, sendo muito importante pesquisar novas formas de mitigação ambiental. No âmbito desta dissertação foram produzidos seis compósitos de IL@MOF com diferentes per-centagens de IL (15 e 30%) no ZIF-8, e os seus respetivos carvões. Os novos materiais foram carac-terizados através de analise elementar, FT-IR, TGA, PXRD e picnometria de hélio. Além disso foram analisadas as capacidades de adsorção e seletividade dos gases (CO2, CH4 e N2). Os resultados de equilíbrio de adsorção mostram que o compósito de 15% de [C6MIM][B(CN)4]@ZIF-8 apresenta boa capacidade de adsorção. No caso dos carvões, o mesmo é observado para o carvão com 15% de [C6MIM][N(CN)2]@ZIF-8. O estudo da seletividade ideal de CO2/CH4 e CO2/N2 nos vários compósitos apresenta resultados bastante promissores. A seletividade ideal de CO2/CH4 e CO2/N2 para os compósitos e respetivos car-vões varia bastante nas diferentes gamas de pressão estudadas. O carvão de compósito de 30% de [C6MIM][B(CN)4]@ZIF-8 apresenta resultados muito altos a baixa pressão (até 1 bar). Adicionalmente os compósitos de 30% de [C6MIM][N(CN)2]@ZIF-8 e de [C6MIM][C(CN)3]@ZIF-8 mostram boa seletivi-dade a pressões mais altas (1-10 bar). Em suma, o estudo proporciona um contributo importante na área de adsorção e seletividade gasosa e oferece oportunidades para a investigação futura dos compósitos e os seus respetivos car-vões. | pt_PT |
| dc.description.abstract | Year after year greenhouse gas emissions increase. CO2 is emitted into the atmosphere from the combustion of fossil fuels and, in the long term, causes environmental, energetic and economic prob-lems. There is a high impact on climate change and it is very important to search for new ways of environmental mitigation. In this dissertation, six IL@MOF composites with different percentages of IL (15 and 30%) were produced at ZIF-8, and their respective carbons. The new materials were characterized through ele-mental analysis, FT-IR, TGA, PXRD and helium pycnometry. In addition, the adsorption capacities and selectivity of gases (CO2, CH4 and N2) were analyzed. The results of adsorption equilibrium show that the 15% composite of [C6MIM][B(CN)4]@ZIF-8 presents good adsorption capacities. In the case of carbons, the same is observed with 15% of [C6MIM][N(CN)2]@ZIF-8. The study of the ideal selectivity of CO2/CH4 and CO2/N2 in several composites shows very prom-ising results. The ideal selectivity of CO2/CH4 and CO2/N2 in the composites and carbons varies signifi-cantly in the different pressure ranges studied. The 30% composite carbon [C6MIM][B(CN)4]@ZIF-8 shows very high results at low pressures (up to 1 bar). Moreover, 30% composites of [C6MIM][N(CN)2]@ZIF-8 and [C6MIM][C(CN)3]@ZIF-8 show good selectivities at higher pressures (1-10 bar). To sum up, the study provides an important contribution in the area of gas adsorption and selec-tivity and offers opportunities for future researches of composites and their respective carbons. | pt_PT |
| dc.identifier.uri | http://hdl.handle.net/10362/135999 | |
| dc.language.iso | por | pt_PT |
| dc.subject | adsorção | pt_PT |
| dc.subject | separação de CO2 | pt_PT |
| dc.subject | líquidos iónicos | pt_PT |
| dc.subject | MOFs | pt_PT |
| dc.subject | carvões derivados de MOF | pt_PT |
| dc.title | Topical IL@MOF-based (ad)sorbents for Gas Separation | pt_PT |
| dc.type | master thesis | |
| dspace.entity.type | Publication | |
| rcaap.rights | openAccess | pt_PT |
| rcaap.type | masterThesis | pt_PT |
| thesis.degree.name | Mestre em Engenharia Química e Bioquímica | pt_PT |