Processamento no estado sólido de compósitos de magnésio com partículas bioativas
| datacite.subject.fos | Engenharia e Tecnologia::Engenharia Mecânica | pt_PT |
| dc.contributor.advisor | Vidal, Catarina | |
| dc.contributor.advisor | Santos, Catarina | |
| dc.contributor.author | Vasilache, Mihail | |
| dc.date.accessioned | 2022-05-24T14:19:36Z | |
| dc.date.available | 2022-05-24T14:19:36Z | |
| dc.date.issued | 2021-12 | |
| dc.description.abstract | O processamento por fricção linear (PFL) é uma tecnologia no estado sólido que permite alterar localmente a microestrutura dos materiais, melhorando as suas propriedades mecânicas à custa de um refinamento de grão. Também permite produzir materiais compósitos com a incorporação de partículas funcionais. O Upward Friction Stir Processing (UFSP) é uma nova abordagem do método de fabrico PFL convencional que promove o fluxo ascendente de material e foi utilizado na produção dos compósitos à base de magnésio. O propósito deste trabalho foi conseguir produzir materiais compósitos de matriz metálica (MCMM) de magnésio (AZ31B) com a incorporação de partículas de hidroxiapatite (HA) para aplicações biomédicas. Foram realizados ensaios para desenvolvimento de parâmetros do processo e avaliaram-se as condições mais favoráveis à execução do processo com refrigeração. Os compósitos obtidos foram sujeitos a uma análise físico-química detalhada. Os resultados obtidos permitiram concluir que é possível produzir compósitos com uma distribuição uniforme de partículas de HA, com um tamanho de grão mais reduzido e uma dureza superior à do magnésio sem partículas. | pt_PT |
| dc.description.abstract | Friction stir processing (FSP) is a solid-state technology which allows localized microstructural modification of materials, thus improving its mechanical properties as a result of grain refinement. The Upward Friction Stir Processing (UFSP) is a new approach to the conventional FSP manufacturing method. The UFSP is based on an upward flow of material, and it was used in the production of composite materials based on magnesium. The goal of this assignment was to demonstrate the ability to produce metal matrix composite materials (MMCM) of magnesium (AZ31B) by incorporating hidroxiapatite (HA) particles for biomedical applications. Different trials have been performed to develop the process parameters and the most favourable conditions to execute it with refrigeration were analysed. The resulting composite materials were subjected to a detailed physicochemical analysis. It was concluded that it is possible to produce composite materials with a uniform distribution of HA particles, with a reduced grain size and a superior hardness when compared to magnesium without particles. | pt_PT |
| dc.identifier.uri | http://hdl.handle.net/10362/138502 | |
| dc.language.iso | por | pt_PT |
| dc.subject | processamento por fricção linear | pt_PT |
| dc.subject | Upward Friction Stir Processing | pt_PT |
| dc.subject | fluxo ascendente | pt_PT |
| dc.subject | materiais compósitos de matriz metálica | pt_PT |
| dc.subject | partículas de hidroxiapatite | pt_PT |
| dc.title | Processamento no estado sólido de compósitos de magnésio com partículas bioativas | pt_PT |
| dc.type | master thesis | |
| dspace.entity.type | Publication | |
| rcaap.rights | openAccess | pt_PT |
| rcaap.type | masterThesis | pt_PT |
| thesis.degree.name | MESTRADO EM ENGENHARIA MECÂNICA | pt_PT |
Ficheiros
Principais
1 - 1 de 1