Production and characterization of Chitin-Glucan Complex by Komagataella pastoris
| datacite.subject.fos | Engenharia e Tecnologia::Engenharia Química | pt_PT |
| dc.contributor.advisor | Reis, Maria d'Ascensão | |
| dc.contributor.advisor | Freitas, Maria Filomena | |
| dc.contributor.author | Chagas, Bárbara Ferreira | |
| dc.date.accessioned | 2016-01-22T10:44:31Z | |
| dc.date.available | 2018-01-22T01:30:14Z | |
| dc.date.issued | 2015-12 | |
| dc.date.submitted | 2016-01 | |
| dc.description.abstract | This thesis was focused on the production, extraction and characterization of chitin:β-glucan complex (CGC). In this process, glycerol byproduct from the biodiesel industry was used as carbon source. The selected CGC producing yeast was Komagataella pastoris (formerly known as Pichia pastoris), due the fact that to achieved high cell densities using as carbon source glycerol from the biodiesel industry. Firstly, a screening of K. pastoris strains was performed in shake flask assays, in order to select the strain of K. pastoris with better performance, in terms of growth, using glycerol as a carbon source. K. pastoris strain DSM 70877 achieved higher final cell densities (92-97 g/l), using pure glycerol (99%, w/v) and in glycerol from the biodiesel industry (86%, w/v), respectively, compared to DSM 70382 strain (74-82 g/l). Based on these shake flask assays results, the wild type DSM 70877 strain was selected to proceed for cultivation in a 2 l bioreactor, using glycerol byproduct (40 g/l), as sole carbon source. Biomass production by K. pastoris was performed under controlled temperature and pH (30.0 ºC and 5.0, respectively). More than 100 g/l biomass was obtained in less than 48 h. The yield of biomass on a glycerol basis was 0.55 g/g during the batch phase and 0.63 g/g during the fed-batch phase. In order to optimize the downstream process, by increasing extraction and purification efficiency of CGC from K. pastoris biomass, several assays were performed. It was found that extraction with 5 M NaOH at 65 ºC, during 2 hours, associated to neutralization with HCl, followed by successive washing steps with deionised water until conductivity of ≤20μS/cm, increased CGC purity. The obtained copolymer, CGCpure, had a chitin:glucan molar ratio of 25:75 mol% close to commercial CGC samples extracted from A. niger mycelium, kiOsmetine from Kitozyme (30:70 mol%). CGCpure was characterized by solid-state Nuclear Magnetic Resonance (NMR) spectroscopy and Differential Scanning Calorimetry (DCS), revealing a CGC with higher purity than a CGC commercial (kiOsmetine). In order to optimize CGC production, a set of batch cultivation experiments was performed to evaluate the effect of pH (3.5–6.5) and temperature (20–40 ºC) on the specific cell growth rate, CGC production and polymer composition. Statistical tools (response surface methodology and central composite design) were used. The CGC content in the biomass and the volumetric productivity (rp) were not significantly affected within the tested pH and temperature ranges. In contrast, the effect of pH and temperature on the CGC molar ratio was more pronounced. The highest chitin: β-glucan molar ratio (> 14:86) was obtained for the mid-range pH (4.5-5.8) and temperatures (26–33 ºC). The ability of K. pastoris to synthesize CGC with different molar ratios as a function of pH and temperature is a feature that can be exploited to obtain tailored polymer compositions.(...) | pt_PT |
| dc.identifier.tid | 101306970 | |
| dc.identifier.uri | http://hdl.handle.net/10362/16311 | |
| dc.language.iso | eng | pt_PT |
| dc.subject | Chitin-glucan complex | pt_PT |
| dc.subject | Komagataella (Pichia) pastoris | pt_PT |
| dc.subject | Industrial wastes/byproducts | pt_PT |
| dc.subject | Glycerol | pt_PT |
| dc.title | Production and characterization of Chitin-Glucan Complex by Komagataella pastoris | pt_PT |