The Influence of Environment in the Alteration of the Stained-Glass Windows in Portuguese Monuments
Publication . Palomar, Teresa; Redol, Pedro; Almeida, Isabel Cruz; da Silva, Eduardo Pereira; Vilarigues, Márcia; VICARTE - Vidro e Cerâmica para as Artes; DCR - Departamento de Conservação e Restauro; MDPI - Multidisciplinary Digital Publishing Institute
This work presents the results of the exposure of soda-lime, potash-lime and mixed-alkali silicate glasses during ten and twenty months in different Portuguese monuments with historical stained-glass windows to characterize the influence of local environmental conditions. The glass samples were exposed in the Monastery of Batalha (Batalha), the Monastery of Jeronimos (Lisbon), and the Cathedral of evora (evora). A set of analytical techniques to assess the physicochemical effects were used, including optical microscopy and Fourier transform infrared spectroscopy. All the samples presented crystalline deposits on their surface; however, their quantity and nature depended on the atmospheric conditions during the days before the collection. Potash-lime silicate glass was the most altered glass in comparison with soda-lime and mixed-alkali silicate glasses. The samples from the Cathedral of evora showed a high content of dust and salts on their surface but without severe chemical pathologies; however, those samples exposed in the Monastery of Jeronimos and the Monastery of Batalha presented alteration layers due to a high humidity environment.
Stained-glass windows of historical buildings from Belém do Pará (Brazil): a conservation approach
Publication . Pinto, Amanda Monteiro Corrêa; Vilarigues, Márcia; Dinis, Maria Filomena
Great part of the architectural heritage from Belém do Pará, a city located in northern
Brazil, has stained-glass windows from the late 19th century onwards of different
provenances. However, the alterations caused by the long exposure to the tropical
environment, typical from the Amazon region, and also by the biodeterioration are still
understudied. It is discussed in the literature review on conservation of stained-glass
windows in Latin America, carried out in this work.
This thesis presents the first study of characterization and biodeterioration of stainedglass of the following historical monuments from Belém: Mausoleum of the family Britto Pontes (BPM), Basilica Santuário de Nazaré (BSN), Church of São Raimundo Nonato (SRN), Museu de Arte Sacra (MAS), and Museu do Estado do Pará (MEP). These monuments are situated in different areas of the city. Three different glass compositions were replicated in laboratory according to historically accurate techniques, in order to be used in two distinct experiments: in situ deterioration and fungal biodeterioration. The analytical techniques used to analyse these experiments were: μ-PIXE, optical microscopy, SEM-EDS and FTIR-ATR.
The μ-PIXE analysis of the historical samples indicated different compositions of sodalime silicate glass with high content of SiO2, composition typically used in the production of modern glass. The Infrared Thermography monitoring of stained glass located in situ, also revealed that fluctuations on the temperature and relative humidity inside the buildings affects mostly the metallic compounds of the panels instead of the glass pieces.
The exposure of replica glass samples to the indoor environments of the five
aforementioned historical monuments, indicated that after 12 months the glass surface
presents a low level of alteration.
The biodeterioration study allowed the characterization of fungi present on the inner
surface of the stained-glass windows from MEP, BPM and BSN. The inoculation was
carried out in the laboratory using spores of four species of fungi previously identified.
The fungi were able to develop dense mycelia in all replica glass samples causing
moderate morphological and chemical alterations at the end of five months.
The results obtained with the experiments proved that the chemical stability of the sodalime glasses guarantees high resistance against hydrolytic and microbiological attacks, even under high temperature and relative humidity. Finally, preventive conservation measures were established in order to safeguard the stained-glass windows of the city of Belém.
Análise de Risco aplicada à Reserva de Mobiliário do Palácio Nacional da Ajuda
Publication . Ramalhinho, Ana Rita Bernardo; Dinis, Maria Filomena; Tavares, Maria José
A realização de uma revisão da literatura sobre modelos e ferramentas de análise de risco aplicados ao património cultural, permitiu concluir que nas últimas duas décadas esta temática tem ganho um maior destaque. A sua utilização tem por objetivo apoiar a tomada de decisão e consequentemente, ajudar à gestão e cuidado do património. A partir dos resultados obtidos, selecionaram-se dois modelos de forma a realizar uma análise de risco à coleção de mobiliário da Reserva Nova do Palácio Nacional da Ajuda (PNA) (Ajuda, Portugal):
• O modelo Cultural Property Risk Analysis (CPRAM), desenvolvido por Robert Waller em 2003, é um modelo semi-quantitativo, e foi selecionado por já ter sido aplicado em outras instituições (e.g. Canadian Museum of Nature, Arquivo Histórico Ultramarino, Museum Amstelkrin, etc.). Define os riscos através de valores numéricos cuja a relação entre si produz a hierarquia das prioridades de risco;
• O modelo QuiskScan é qualitativo, foi desenvolvido por Agnes Brokerhof e Anna Bülow em 2016, e selecionado por ser muito recente e não existirem, até à data, outros trabalhos em que tenha sido aplicado. Define as prioridades dos riscos de uma forma não numérica a partir de categorias (“Alto”, “Médio” e “Baixo”).
A aplicação dos dois modelos permitiu chegar a uma hierarquização dos principais riscos genéricos para a coleção em estudo, sendo os mais prioritários: Fogo, Forças Físicas e Pragas. No entanto, para a proposta de soluções de mitigação, recorreu-se aos riscos específicos identificados pelo modelo CPRAM, onde, por exemplo, para o risco de ocorrência de um incêndio na área de reserva com consumo da coleção completa, propõe-se a instalação de mais extintores e expressores; para o risco da queda de objetos das estantes, propõe-se a colocação de uma fita em torno das estantes; e para o risco de infestação por insetos é proposta a desinfestação dos objetos por anoxia.
Assim, sugere-se que numa instituição onde nunca se realizou uma análise de risco, se aplique inicialmente o modelo QuiskScan (de aplicação mais rápida) e posteriormente, conhecendo os principais riscos genéricos, se utilize o CPRAM com o intuito de propor soluções de mitigação (a partir da identificação e cálculo dos riscos específicos). Isto permitirá reduzir o tempo e otimizar os recursos.
Unidades organizacionais
Descrição
Palavras-chave
Contribuidores
Financiadores
Entidade financiadora
Fundação para a Ciência e a Tecnologia
Programa de financiamento
6817 - DCRRNI ID
Número da atribuição
UID/EAT/00729/2013